Unlike appearance prototypes produced in weak materials, Dimension parts built in ABS or ABS Plus (acrylonitrile butadiene styrene) have been used for functional and field tests - from wind tunnel testing to camera mounts on a M2 Bradley tank and a spray gun running at 60 psi.
For use with your BST 768, SST 768, BST 1200, or SST 1200.
DO NOT PURCHASE IF YOU OWN A BST 1200 ES, SST 1200 ES, OR ELITE. IF YOU OWN ONE OF THESE MACHINES PURCHASE P430 MATERIAL.
ABS-P400 Material Properties
| Mechanical Properties | Test Method | English |
Metric |
| Tensile Strength (Type 1, 0.125", 0.2"/min) | ASTM D638 | 3,200 psi | 22 MPa |
| Tensile Modulus (Type 1, 0.125", 0.2"/min) | ASTM D638 | 236,000 psi | 1,627 MPa |
| Tensile Elongation (Type 1, 0.125", 0.2"/min) | ASTM D638 | 6% | 6% |
| Flexural Delamination | ASTM D790 | 2,000 psi | 14MPa |
| Flexural Strength (Method 1, 0.05"/min) | ASTM D790 | 6,000 psi | 41 MPa |
| Flexural Modulus (Method 1, 0.05"/min) | ASTM D790 | 266,000 psi | 1,834 MPa |
| IZOD Impact, notched (Method A, 20°C) | ASTM D256 | 2.0 ft-lb/in |
106 J/m |
| Thermal Properties |
Test Method |
English |
Metric |
| Heat Deflection (HDT) @ 66 psi | ASTM D648 | 195°F | 90°C |
| Heat Deflection (HDT) @ 264 psi | ASTM D648 | 169°F | 76°C |
| Glass Transition Temperature (Tg) | DMA (SSYS) | 219°F | 104°C |
| Melt Point | ------- | Not Applicable | Not Applicable |
| Coefficient of Thermal Expansion | ASTM E831 | 5.60 E-05 in/in°F | ------- |
| Other |
Test Method |
Value |
| Specific Gravity | ASTM D792 | 1.04 |
| Vertical Burn | UL94 | HB |
| Dielectric Strength | IEC 60112 | 32.0 kV/mm |
| System Availability |
Layer Thickness Capability |
Support Structure |
Available Colors |
|
Dimension SST 768 |
0.013 inch (0.330 mm) 0.010 inch (0.254 mm) |
Soluble Supports (SST 768 and SST 1200) Breakaway Supports (BST 768 and BST 1200) |
White Black Steel Grey Red Blue Green Yellow |